求翻译：A.So the induced β crystals obtained by α-row nuclei in PP1 are fewer too. The growth rate of β crystals is faster than that of α crystals at 134 °C; therefore, these induced β crystals restrain the growth of α crystals. In PP0, the oriented α crystals are larger, the induced β crystals are also larger, and the restrai是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
A.So the induced β crystals obtained by α-row nuclei in PP1 are fewer too. The growth rate of β crystals is faster than that of α crystals at 134 °C; therefore, these induced β crystals restrain the growth of α crystals. In PP0, the oriented α crystals are larger, the induced β crystals are also larger, and the restrai
问题补充： |
|
2013-05-23 12:21:38
a.so由α-行晶核在PP1中获得的诱导β晶体少太多。 β晶体的生长速率比α结晶的速度在134℃，因此，这些诱导的β晶体抑制α晶体的生长。在PP0，取向α晶体是越大，诱导β晶体也较大，α晶体的生长的抑制程度比在PP1大得多。这样的α-晶体的结晶度在PP0比在PP1在这些剪切速率下。当剪切速率大于20秒-1，PP0的α结晶度接近于PP1的。表2证实，在PP1β晶体的生长机理几乎是一样的，在PP0的结果。在PP1添加剂的存在抑制了剪切诱导的β晶体的形成。
|
|
2013-05-23 12:23:18
A.So在PP1的α行中坚力量获得的导致的β水晶也是少量。β水晶的增长率比那快速α水晶在134 °C;因此，这些导致的β水晶克制α水晶成长。在PP0，针对的α水晶是更大，导致的β水晶也是更大，并且α水晶成长的被克制的程度大于那在PP1。因此在PP0的α水晶结晶性低于那在PP1以这些剪率。
|
|
2013-05-23 12:24:58
A.So α列中坚力量获得的导致的β水晶在PP1也是较少。 β水晶生长率比那快速α水晶在134 °C; 因此，这些导致的β水晶克制α水晶成长。 在PP0，针对的α水晶是大，导致的β水晶也是更大，并且α水晶成长的被克制的程度大于那在PP1。 如此α水晶结晶性在PP0低于那在PP1以这些剪率。 当剪率超出20 s-1时， PP0 α结晶性是紧挨那PP1。 表2的结果证实β水晶成长机制在PP1几乎是相同象那在PP0。 添加剂的存在PP1克制了剪导致的β水晶的形成。
|
|
2013-05-23 12:26:38
A.So 获得的 α-行核的 PP1 的诱导的 β 晶体也较少。Β 晶体的增长率是速度比 α 晶体的 134 ° C;因此，这些诱导 β 晶体抑制 α 晶体的生长。在 PP0，面向的 α 晶体较大、 诱导的 β 晶体也是更大，和克制的 α 晶体的生长程度比大得多，在 PP1。所以 α-水晶结晶程度，PP0 是比，在搜索这些 PP1 剪切速率低。当剪切速率超过 20 s 1 时，α 结晶度 PP0 很近，PP1表 2 的结果证实 PP1 β 晶体的生长机制是几乎相同的 PP0。存在的添加剂在 PP1 克制剪切诱导 β 晶体的形成。
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区