求翻译：Fig. 2 shows the XRD patterns of the composite materials with three different diatomite concentrations, 25%, 35% and 45%. The measure-ments were done after the composite was sintered. One can see from the figure that the main phases in all the three composite materials are quartz and sodium sulfate. All the peaks in th是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
Fig. 2 shows the XRD patterns of the composite materials with three different diatomite concentrations, 25%, 35% and 45%. The measure-ments were done after the composite was sintered. One can see from the figure that the main phases in all the three composite materials are quartz and sodium sulfate. All the peaks in th
问题补充： |
|
2013-05-23 12:21:38
正在翻译，请等待...
|
|
2013-05-23 12:23:18
图2显示合成材料的XRD样式与三不同硅藻土含量的， 25%， 35%和45%。在综合被焊接了后，测量完成。一能从图看到在所有三种合成材料的主要阶段是石英和硫酸钠。在三个XRD样式的所有峰顶显示一对一的位置书信和新的峰顶没有被观察。然而，不同的白云岩含量给不同的峰值强度。
|
|
2013-05-23 12:24:58
。 2个展示合成材料的XRD样式以三不同硅藻土集中， 25%， 35%和45%。 在综合被焊接了之后，测量完成。 你能从图看主要阶段在所有三种合成材料是石英和硫酸钠。 所有峰顶在三个XRD样式显示一对一位置书信和新的峰顶没有被观察。 然而，不同的白云岩含量给不同的高峰强度。 在硫酸钠集中或减退的增量在硅藻土集中导致在衍射强度的增量特别在 (113) 飞机以一个高峰位置2θ = 33.9°。 硅藻土主要绕射的峰顶的强度发生在2θ = 26.5°，对应于 (101) 飞机，表明重大减退以越来越少的硅藻土集中。 这些结果建议形状安定材料、硅藻土和相变材料，硫酸钠，是高度化工兼容的在高温。 仅物理变动
|
|
2013-05-23 12:26:38
图 2 显示了与三个不同的硅藻土浓度时，复合材料的 x 射线衍射模式 25%、 35%和 45%。测值反演进行了复合材料烧结后。人们可以看到从图中所有三种复合材料的主要阶段是石英和硫酸酯钠盐。在所有山峰中三的 x 射线衍射模式都显示一对一的位置对应并没有产生新的峰观察。然而，不同的白云石浓度给不同的峰值强度。硫酸酯钠盐浓度增加或减少的硅藻土浓度导致增加，特别是在 2t 峰值位置 （113） 平面衍射强度 = 33.9 °。硅藻土主要衍射峰的强度发生在 2t = 26.5 °，对应 （101） 的飞机，指示与降低硅藻土浓度显著降低。这些结果表明形状稳定材料、 硅藻土、 和相变材料，硫酸酯钠盐，是
|
|