求翻译:In order to enhance the possible phase separation in the rapidly quenched HEA, the as-spun alloy was annealed at an intermediate temperature of 500 C for 1 h in a tube furnace in a mixed protective atmosphere of H2 and Ar, followed by slow cooling.是什么意思?![]() ![]() In order to enhance the possible phase separation in the rapidly quenched HEA, the as-spun alloy was annealed at an intermediate temperature of 500 C for 1 h in a tube furnace in a mixed protective atmosphere of H2 and Ar, followed by slow cooling.
问题补充: |
|
2013-05-23 12:21:38
为了提高在快速淬火HEA的可能的相分离,则由于纺出合金进行退火在500中间温度?下,在管式炉中H 2和Ar的混合保护气氛1小时,随后缓慢冷却
|
|
2013-05-23 12:23:18
正在翻译,请等待...
|
|
2013-05-23 12:24:58
为了提高可能的分相在迅速地熄灭的HEA,和转动的合金在辐射管烧成炉锻炼在一个中间温度500 C为1 h在H2和Ar混杂的防护大气,跟随由缓慢冷却。
|
|
2013-05-23 12:26:38
为了提高中快速淬火 HEA 的可能相分离,作为纺合金退火在中间温度为 500 ℃ 为 1 h 在管炉中 H2 和 Ar,其次是缓慢冷却的混合保护气氛。
|
|
2013-05-23 12:28:18
In order to enhance the possible phase separation in the rapidly quenched HEA, the as-spun alloy was annealed at an intermediate temperature of 500 C for 1 h in a tube furnace in a mixed protective atmosphere of H2 and Ar, followed by slow cooling.
|