求翻译：In general, increasing particle size will reduce the contact surface between powders and restrain the formation of ZrC and ZrB2,though the value of G◦for Eq. (1) is negative. As B4C reaches14 m, the maximum peak temperature corresponding to theZr–B4C reaction is above 1182◦C because high temperature favorsthe reactiv是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
In general, increasing particle size will reduce the contact surface between powders and restrain the formation of ZrC and ZrB2,though the value of G◦for Eq. (1) is negative. As B4C reaches14 m, the maximum peak temperature corresponding to theZr–B4C reaction is above 1182◦C because high temperature favorsthe reactiv
问题补充： |
|
2013-05-23 12:21:38
通常，增加粒度会降低粉末之间的接触面，抑制的ZrC和ZrB2的形成，虽然？G◦for公式的值。
|
|
2013-05-23 12:23:18
正在翻译，请等待...
|
|
2013-05-23 12:24:58
正在翻译，请等待...
|
|
2013-05-23 12:26:38
一般情况下，粒子大小的增加将减少接触表面间粉末，并抑制形成 ZrC 和 ZrB2，虽然 G◦for 方程 （1） 值为负。作为 B4C reaches14 m，对应于 theZr — — B4C 反应的最大峰值温度是上文 1182◦C 因为高温度总是宠爱那些反应性的粉末，往往是不完整的低于 1250◦C(Fig.4b)。其结果是，更多的锆仍然在 DSC 的产品和由此产生的 ZrC ZrB2decreased (图 5b）。进一步增加大小的 B4C 到 28 米结果在低迷的固体 reactionbetween 锆和 B4C。这产生了小小的 ZrC 和 ZrB2 （图 5 c）。小数量的热发布经
|
|
2013-05-23 12:28:18
正在翻译，请等待...
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区