求翻译：RuO2 nanostructures were synthesized by heating Ru nanoparticles in air at 280 degrees C using Cu as catalyst. The Ru nanoparticles were prepared by the pyrolysis of ruthenium precursors in a vacuum using multi-walled carbon nanotubes as templates. The RuO2 nanostructures grew radically with diameters of 50-150 nm, and是什么意思？ 待解决
 悬赏分：1
- 离问题结束还有
RuO2 nanostructures were synthesized by heating Ru nanoparticles in air at 280 degrees C using Cu as catalyst. The Ru nanoparticles were prepared by the pyrolysis of ruthenium precursors in a vacuum using multi-walled carbon nanotubes as templates. The RuO2 nanostructures grew radically with diameters of 50-150 nm, and
问题补充： |
|
2013-05-23 12:21:38
合成了在使用Cu作为催化剂280摄氏度的空气中加热钌纳米颗粒的RuO2纳米结构。
|
|
2013-05-23 12:23:18
密多心经2纳米构造合是综合了暖气RU纳米微粒在空气在280°℃使用CU作为催化剂。 纳米微粒的RU编写了钌高温分解的前体在一个真空使用多壁碳纳米管为模板。 2岁的纳米构造合增长从根本上,直径50纳米制程和长度的0.5m2MU。 纳米结构的增长主要取决于纳米微粒dispersivity RU的mwnts上。
|
|
2013-05-23 12:24:58
RuO2 nanostructures通过加热Ru nanoparticles在空气综合在280摄氏度使用Cu作为催化剂。 Ru nanoparticles由钌前体加热分解在真空准备使用多被围住的碳nanotubes作为模板。 RuO2 nanostructures根本地增长以0.5-2.0 mu m.的直径50-150毫微米和长度。 nanostructure成长在MWNTs主要依靠Ru nanoparticles dispersivity。 这些nanostructures电化学物产由循环伏安法学习。
|
|
2013-05-23 12:26:38
通过加热空气在 280 ℃ 使用铜作为催化剂中的钌纳米合成了 RuO2 纳米结构。钌纳米制得的钌前体在多壁碳纳米管用作模板的真空热解。RuO2 纳米结构从根本上随着 50-150 毫微米，直径和长度的 0.5-2.0 万亩。纳米结构的增长主要取决于钌纳米碳纳米管上的分散性。采用循环伏安法研究了这些纳米结构的电化学性能。
|
|
2013-05-23 12:28:18
RuO2 毫微组织被以 280 度在空中把 Ru 毫微微粒加热合成使用 Cu 的 C 作为催化剂。Ru 毫微微粒在使用多墙碳毫微管子的真空在 ruthenium 先驱者的高温分解旁边准备作为模板。RuO2 毫微组织根本上有直径的 50-150 nm 生长，长度的 0.5-2.0 亩 m。毫微结构的成长主要在 MWNTs 依赖于 Ru 毫微微粒的分散。这些毫微结构的电气化学的财产被循环的 voltammetry 学习。
|
湖北省互联网违法和不良信息举报平台 | 网上有害信息举报专区 | 电信诈骗举报专区 | 涉历史虚无主义有害信息举报专区 | 涉企侵权举报专区